BESTNYL SI00VI02BH14
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aQT4zP_BESTNYL-SI00VI02BH14.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 black with 20% mineral charge and heat stabilized is characterized for its great dimensional stability, good superficial finish, good in machine and release mould behaviour. Currently used in injection pieces that are not required to endure mechanical efforts, but with a great deal of importance in final appearance and dimensionality. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ISO 62 |
| Ash Content | 20 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 79 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2 |
| Tensile Stress | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 220 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 225 to 240 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil MED10-4161 | NuSil Technology | Silicone | NuSil |
| NOVALAC RX®865M | Vyncolit N.V. | Phenolic | NOVALAC |
| Formolene® HB5202B | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| Indothene CC | Reliance Industries Limited | LDPE | Indothene |
| Karina WHITE PVC COMPOUND -E500-10/1-BT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |