Generic PUR-MDI
| Category: | PUR-MDI , Polyurethane (MDI) |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aQR0gt_Generic-PUR-MDI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PUR-MDI This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.0450 to 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 28 to 76 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Break, 23°C | 3.79 to 24.5 | MPa | |
| 23°C | 0.0870 to 0.161 | MPa | |
| Tensile Elongation (Break, 23°C) | 4.2 to 11 | % | ASTM D638 |
| Flexural Modulus (23°C) | 103 to 1590 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 6.55 to 49.9 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 1.48 to 10.6 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 1.20 to 5.42 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 170 to 420 | % | ASTM D412 |
| Tear Strength (23°C) | 0.123 to 19.8 | kN/m | ASTM D624 |
| Bayshore Resilience | 17 to 81 | % | ASTM D2632 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 3.8 to 25 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 11 to 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 69.8 to 109 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Mix Viscosity | 297 to 778 | cP | ASTM D2393 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density (23°C) | 1.05 to 1.08 | g/cm³ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 400 HI SI 1 | RTP Company | PS Alloy | RTP |
| ACCUTECH™ HP0339W10L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Forprene® 6SD001A65 | SO.F.TER. SPA | TPV | Forprene® |
| Hytrel® DYM250S BK472 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Hostacom CR 250 F C21451 | LyondellBasell Industries | PP, Unspecified | Hostacom |