LEXAN™ FXE4271L resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aQCD08_LEXAN-FXE4271L-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN FXE4271L is a 10% glass filled, impact modified polycarbonate with excellent light-shield capability. It is designed for high flow, superior surface appearance, enhance release and good impact ductility. FXE4271L is available in white color only and ideal for light-shield applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.30 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.13 | % | |
| Equilibrium, 23°C, 50% RH | 0.040 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3850 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 48.0 | MPa | |
| Break | 37.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 4.0 | % | |
| Break | 11 | % | |
| Flexural Modulus 4(50.0 mm Span) | 3600 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 87.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1900 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 36.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 127 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 120 | °C | |
| Vicat Softening Temperature | 132 | °C | ISO 306/B120 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 266 to 288 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 288 to 310 | °C | |
| Nozzle Temperature | 282 to 304 | °C | |
| Processing (Melt) Temp | 288 to 310 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FE-361U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| INSPIRE™ TF0808 | Trinseo | TPO | INSPIRE™ |
| Plaslube® J-50/10/TF/15 NAT | Techmer Engineered Solutions | PC | Plaslube® |
| Plexar® PX3216 | LyondellBasell Industries | LLDPE | Plexar® |
| Adflex Q 108 F | LyondellBasell Industries | TPO (POE) | Adflex |