Hifax TRC 134P C11306
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aQ6mdX_Hifax-TRC-134P-C11306.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP/EPR-Blend, mineralfilled, impact modified, UV-stabilized, with ultra low shrinkage and very high flowability for unpainted exterior applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2554 | ||
| Across Flow : 23°C, 48 hr | 0.60 | % | |
| Flow : 23°C, 48 hr | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1300 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 17.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 500 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1500 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Drop Test 2(-20°C) | Ductile Break | DIN 53443 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mold Shrinkage Pressure | 4.00 | MPa | ISO 2554 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 45 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (23 to 80°C) | 4.2E-5 | cm/cm/°C | DIN 53752 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | weld line, 18.2 kg, h=1m, d=3mm, clamp, no fat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 92682 A | RTP Company | Nylon 6 | RTP |
| RTP 905 TFE 15 | RTP Company | PSU | RTP |
| Moplen PP200P | LyondellBasell Industries | PP Random Copolymer | Moplen |
| VESTAMID® L L-GB30 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| HiFill® PA6/6 GF14 IM HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |