Nypol® PA A3 G13 HS UV RH PRTA011 NR409
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aOKHiU_Nypol-PA-A3-G13-HS-UV-RH-PRTA011-NR409.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6.6 in black color reinforced with 13% glass fibre ,heat stabilised, UV and hydrolysis resistant, good set of mechanical properties. Ideal for molding for injection. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.23 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 2.3 | -- | % | ASTM D570 |
| Ash Content | 11 to 15 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | 3600 | MPa | ASTM D638 |
| Tensile Strength | 119 | 76.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 12 | % | ASTM D638 |
| Flexural Strength | 165 | 115 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -30°C | 40 | 30 | J/m | |
| 23°C | 40 | 55 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 258 | -- | °C | |
| 1.8 MPa, Unannealed | 235 | -- | °C | |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | ASTM D257 |
| Electric Strength (2.00 mm) | 25 | -- | kV/mm | IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PE RPE10HW14BK | Ferro Corporation | PE, Unspecified | Ferro PE |
| INSTRUC PSGF15 | Infinity LTL Engineered Compounds | PS (GPPS) | INSTRUC |
| Karina COMP. PVC CRYSTAL -E 85/253-IS-SI-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Moplen HP504N | LyondellBasell Industries | PP Homopolymer | Moplen |
| apilon 52® D1 40 | API SpA | TPU-Polyester | apilon 52® |