Ryton® QC160P
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ryton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aOKAtK_Ryton-QC160P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ryton® QC160P (pelletized) polyphenylene sulfide exhibits excellent thermal stability and chemical resistance and is suitable for thermoplastic extrusion processes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(316°C/5.0 kg) | 45 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Ash Content | 0.3 | wt% | ISO 3451-1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Volatiles (150°C) | < 0.3 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2 |
| Tensile Stress | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 3400 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 53 | J/m | ASTM D256 |
| -- | 4.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 95.0 | °C | |
| Glass Transition Temperature | 90.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | > 180 | °C | ISO 306 |
| Melting Temperature | 280 | °C | ISO 11357-3 |
| CLTE - Flow | ASTM E831 | ||
| -50 to 50°C | 5.0E-5 | cm/cm/°C | |
| 100 to 200°C | 1.2E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.30 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (25°C, 1 MHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (25°C, 1 MHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by CP Chemical) | V-0 | UL 94 | |
| Oxygen Index | 44 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene F24-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| AKROMID® A3 1 FR black (3051) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Heraform® R1300 NAT | Radici Plastics | Acetal (POM) Copolymer | Heraform® |
| Hytrel® SC969 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| LUBAN™ 1101 N | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |