| Trilliant™ HC high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Trilliant™ HC blends made with Tritan™ copolyester are available in standard grades or can be customized to meet specific performance requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.56 | % | |
| Across Flow : 3.18 mm | 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1740 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 2 | 41.4 | MPa | |
| Break 3 | 23.4 | MPa | |
| Tensile Elongation 4(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 5 | 1900 | MPa | ASTM D790 |
| Flexural Strength 6 | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 850 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 94.0 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 80.0 | °C | |
| CLTE - Flow (-30 to 30°C) | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 51 mm/min |
| 5 . | 13 mm/min |
| 6 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE DM500 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| Spartech Polycom E65450 | Spartech Polycom | PVC, Unspecified | Spartech |
| Moplen EP548P | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| WPP PP M 2097-004 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| BCC Resins BC 7136-2 | BCC Products Inc. | Epoxy | BCC Resins |