Torayca® 2701T-30V
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torayca® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aO3YG2_Torayca-2701T-30V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torayca® 2701T-30V is a Polyamide 610 (Nylon 610) product filled with 20% carbon fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.50 | % | |
| Flow : 3.00 mm 2 | 0.10 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 264 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.2 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 20000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 398 | MPa | ISO 178 |
| Amount of Wear - vs. S45C 3 | 0.300 | mg/hr | Suzuki Method |
| Coefficient of Friction - vs. S45C 4 | 0.360 | Suzuki Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | DSC |
| CLTE - Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 1MPa, 0.33 m/s |
| 4 . | 1MPa, 0.33 m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex NT0320GB | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| LNP™ LUBRICOMP™ CL001I compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ LUBRICOMP™ |
| PermaStat® 2503 | RTP Company | PC+ABS | PermaStat® |
| Sylvin 8362-75 Brown 7438 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ STAT-KON™ KE002 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ STAT-KON™ |