NORYL PPX™ PPX830 resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL PPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aNaUC5_NORYL-PPX-PPX830-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus of 7600 MPa; this grade has been developed for application where dimension stability, temperature and chemical resistance could be required. NORYL PPX830 is an opaque material available in limited colors only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.25 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7600 | MPa | ASTM D638 |
| -- | 7700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 101 | MPa | ASTM D638 |
| Yield | 98.0 | MPa | ISO 527-2/5 |
| Break 3 | 101 | MPa | ASTM D638 |
| Break | 98.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.9 | % | ASTM D638 |
| Yield | 3.2 | % | ISO 527-2/5 |
| Break 5 | 100 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6600 | MPa | ASTM D790 |
| -- 7 | 7100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 141 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 144 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 9 | ISO 179/1eU | ||
| -30°C | 36 | kJ/m² | |
| 23°C | 39 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 95 | J/m | ASTM D256 |
| 23°C 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D4812 |
| -30°C 11 | 42 | kJ/m² | ISO 180/1U |
| 23°C 12 | 42 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 10.0 | J | |
| 23°C, Total Energy | 15.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 166 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 13 | 168 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 156 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 153 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 150 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 95°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 95°C | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -30 to 80°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 to 75.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 245 to 290 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 255 to 290 | °C | |
| Nozzle Temperature | 260 to 300 | °C | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 40.0 to 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TiGlaze™ ST | Eastman Chemical Company | Copolyester | TiGlaze™ |
| NEFTEKHIM PP 4210G (EP2S30B) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Geon™ BIO RA9000 | PolyOne Corporation | PVC, Flexible | Geon™ BIO |
| HDPE NG 7000 H | The Dow Chemical Company | HDPE | HDPE |
| Osterlene® LLB0918A | Osterman & Company | LLDPE | Osterlene® |