HiFill FR® PA6/6 FR HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill FR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aNT1xN_HiFill-FR-PA6-6-FR-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill FR® PA6/6 FR HS is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.3 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 20 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648 |
| CLTE - Flow | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 27 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| TPCI # | 9857101 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | > 6.0 | hr | |
| Rear Temperature | 254 to 277 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ M4800NS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| SUPREME HIPS SH 810 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| AKROMID® B3 GF 45 1 natural (3983) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| DeWAL DW 211 | DeWAL Industries | PTFE | DeWAL |
| Hostacom TKS708D | LyondellBasell Industries | TPO (POE) | Hostacom |