NEALID XG300
| Category: | Nylon+Olefin , Polyamide + Polyolefin |
| Manufacturer: | AD majoris |
| Trademark: | NEALID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aN082f_NEALID-XG300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEALID XG300 is a 30 % glass fibre reinforced polyamide alloy intended for Injection moulding. APPLICATIONS NEALID XG300 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. NEALID XG300 is available in both black (NEALID XG300 - 8229) and natural (NEALID XG300) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.28 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.90 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8500 | 7800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 5.5 | % | ISO 527-2 |
| Flexural Modulus | 7600 | 7000 | MPa | ISO 178 |
| Flexural Stress | 175 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -20°C | -- | 9.0 | kJ/m² | |
| 23°C | 13 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -20°C | -- | 30 | kJ/m² | |
| 23°C | 41 | 45 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 186 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| CLTE - Flow | 2.7E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+15 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4787 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| AKROMID® B3 GF 50 1 black (2488) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Aristech Solarcast® | Aristech Acrylics LLC | Acrylic, Unspecified | Aristech |
| Ferro PP NPP00GC25WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hifax TSOP EM1 G63083 | LyondellBasell Industries | PP Impact Copolymer | Hifax |