SABIC® HDPE P6006N
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aMXarF_SABIC-HDPE-P6006N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Provisional Data Sheet P6006N is a grade which has a high density (class MRS 10 - PE 100) and a bimodal distribution of the molecular mass. An universal grade for pipe extrusion which, due to a keen combination of properties. it can be used for telecommunication, corrugated and spiral pipes. P6006N is a natural High Density Polyethylene (HDPE) resin specifcally designed for Pipe Extrusion. It provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.949 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 6.2 | g/10 min | |
| 190°C/5.0 kg | 0.23 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 850 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress (Yield, 2.00 mm, Compression Molded) | 23.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Yield, 2.00 mm, Compression Molded) | 10 | % | ISO 527-2/1BA/50 |
| Flexural Creep Modulus - 4 point, 1 min-value | 1.05 | GPa | DIN 19537-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | > 20 | min | EN 728 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 74.0 | °C | ISO 306 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) M/HI | A. Schulman Europe | ABS | POLYMAN® |
| NaturePlast NP BF 001 | NaturePlast | Biodeg Polymers | NaturePlast |
| NEXUS Reprocessed Nylon 66 G33 RBK | Nexus Resin Group, LLC. | Nylon 66 | NEXUS Reprocessed |
| Chemical Resources ABS1200 | Chemical Resources, Inc. | ABS | Chemical Resources |
| Plaslube® PA6/6 GF40 IM HS L BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |