CYCOLAC™ EXABS01 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aM73oS_CYCOLAC-EXABS01-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sheet extrusion ABS with medium impact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2030 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 39.3 | MPa | ASTM D638 |
| Fracture | 29.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.1 | % | ASTM D638 |
| Fracture | 32 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2100 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 63.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 280 | J/m | ASTM D256 |
| 23°C | 410 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 33.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 93.3 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 80.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 7 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 100 sec^-1) | 1400 | Pa·s | ASTM D3835 |
| Extrusion instructions |
|---|
| Extrusion Blow Molding Parameters: Adapter - Zone 5 Temperature: 210 - 232 °C Barrel - Zone 1 Temperature: 204 - 227 °C Barrel - Zone 2 Temperature: 204 - 227 °C Barrel - Zone 3 Temperature: 204 - 227 °C Barrel - Zone 4 Temperature: 204 - 227 °C Die Temperature: 216 - 235 °C Drying Temperature: 82 - 88 °C Drying Time: 4 - 5 hrs Drying Time (Cumulative): 24 hrs Extruder Feed Zone Temperature: 60 - 77 °C Head - Zone 6 - Top Temperature: 216 - 232 °C Head - Zone 7 - Bottom Temperature: 216 - 232 °C Maximum Moisture Content: 0.02 % Melt Temperature (Parison): 216 - 232 °C Mold Temperature: 38 - 82 °C Screw Speed: 20 - 60 rpm Sheet Extrusion Parameters: Adapter Temperature: 204 - 249 °C Barrel - Zone 1 Temperature: 171 - 199 °C Barrel - Zone 2 Temperature: 182 - 221 °C Barrel - Zone 3 Temperature: 188 - 227 °C Barrel - Zone 4 Temperature: 199 - 238 °C Die Temperature: 204 - 249 °C Drying Temperature: 82 - 93 °C Drying Time: 4 hrs Maximum Moisture Content: 0.02 % Melt Temperature: 216 - 260 °C Roll Stack Temp - Bottom: 99 - 104 °C Roll Stack Temp - Middle: 93 - 104 °C Roll Stack Temp - Top: 88 - 93 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| 7 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GSF25/15-66 22L-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Delrin® 100ST BK602 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| ELASTOSIL® FLR 3905/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® FLR |
| EcoPaXX® Q-X07209 | DSM Engineering Plastics | Nylon 410 | EcoPaXX® |
| EOS PA 2241 FR | EOS GmbH | Nylon 12 | EOS |