PAmpellonne® rgr_ss
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Politem Plastik Ltd. |
| Trademark: | PAmpellonne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aL9pX5_PAmpellonne-rgr-ss.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| All Politem Plastik Polyamide Resins are recycled from Post Industrial Fiber Waste Streams |
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 to 1.15 | g/cm³ | ISO 1183 |
| Ash Content | 0.50 to 0.80 | % | ISO 3451-4 |
| Moisture | 0.10 to 0.70 | % | ISO 15512/B |
| Relative Viscosity 1 | 2.40 to 2.50 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| DSC Analysis | > 95 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 to 100 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 to 4000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 to 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 to 6.0 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 263 to 271 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Formic |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® E 70 LF | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Ultramid® A3UG5 | BASF Corporation | Nylon 66 | Ultramid® |
| Grilamid® LV-23 ESD | EMS-GRIVORY | Nylon 12 | Grilamid® |
| LEXAN™ 923X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina GREEN PVC COMPOUND -E 911D40/ 77-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |