ULTEM™ DT1810EV resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aKaTTk_ULTEM-DT1810EV-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 43 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 56.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.36 | % | |
| Equilibrium, 23°C, 50% RH | 0.080 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3210 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 103 | MPa | ASTM D638 |
| Yield | 98.0 | MPa | ISO 527-2/5 |
| Break 3 | 85.0 | MPa | ASTM D638 |
| Break | 80.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/5 |
| Break 5 | 80 | % | ASTM D638 |
| Break | 80 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3320 | MPa | ASTM D790 |
| -- 7 | 3100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 135 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 35 | J/m | ASTM D256 |
| 23°C | 32 | J/m | ASTM D256 |
| -30°C 10 | 2.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ASTM D4812 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 48.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 173 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 178 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 12 | 168 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 192 | °C | ASTM D1525, ISO 306/B50 11 13 |
| -- | 195 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 150°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 150°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 310 to 332 | °C | |
| Middle Temperature | 321 to 343 | °C | |
| Front Temperature | 332 to 354 | °C | |
| Nozzle Temperature | 327 to 349 | °C | |
| Processing (Melt) Temp | 332 to 354 | °C | |
| Mold Temperature | 93.3 to 135 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA6 A 1000/310 IM | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Anjacom® J255-H/GF30 | Almaak International GmbH | Nylon 6 | Anjacom® |
| Diamond ABS 3501 E Black 1300 | Network Polymers, Inc. | ABS | Diamond ABS |
| HiFill® TPX-HTN-01026 A | Techmer Engineered Solutions | Nylon, Unspecified | HiFill® |
| Sylvin 8707-84 Grey 9528 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |