POLYMAN® (SAN) 29/10
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYMAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aKExLc_POLYMAN-SAN-29-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Good flow SAN grade with high chemical resistance |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 10.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 171 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ISO 306/A50 |
| -- | 102 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 100 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 30.0 to 90.0 | MPa | |
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | < 600 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-FRHG30 | Polymer Resources Ltd. | PBT | PRL |
| Spartech Polycom SCR5-2010 | Spartech Polycom | PP Copolymer | Spartech |
| Monprene® MP-1852 | Teknor Apex Company | TPE | Monprene® |
| NuSil MED-4850 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| ICORENE® - Semi Conductives 1761 SC Black 9002 | ICO Polymers EMEA, A Division of A. Schulman | mMDPE | ICORENE® |