EPO-TEK® E3035T-2
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aKARtv_EPO-TEK-E3035T-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® E3035T-2 is a single component, silver-filled epoxy for semiconductor die attach, as well as SMD attach on hybrid circuits. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 62 | ppm | |
| K+ | 3 | ppm | |
| Na+ | 21 | ppm | |
| NH4+ | 24 | ppm | |
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 390 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus | 2.55 | GPa | |
| Thixotropic Index | 4.09 | ||
| Weight Loss on Heating | |||
| 200°C | 0.15 | % | |
| 250°C | 0.29 | % | |
| 300°C | 0.32 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 100 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.2E-5 | cm/cm/°C | |
| -- 3 | 8.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 1.4 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life (-40°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Silver | ||
| Density | 1.13 | g/cm³ | |
| Viscosity 4(23°C) | 80 to 120 | Pa·s | |
| Curing Time (180°C) | 1.0 | hr | |
| Pot Life | 40000 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ||
| Lap Shear Strength (23°C) | 12.2 | MPa | |
| Volume Resistivity (23°C) | < 5.0E-4 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 2.5 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 A TFE 10 | RTP Company | Nylon 6 | RTP |
| DOMAMID® 6G30V0A | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| LUVOCOM® 50-8907 | Lehmann & Voss & Co. | PC | LUVOCOM® |
| Lupox® TE5000HZ | LG Chem Ltd. | PC+PBT | Lupox® |
| Braskem PE GP100BKXP | Braskem | HDPE | Braskem PE |