Michiloy MT11220
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michiloy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aIRTYB_Michiloy-MT11220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michiloy MT11220 is a Polycarbonate + PBT (PC+PBT) product. It is available in North America. Primary characteristic: impact resistant. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 49.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus - Tangent | 1720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 116 | °C | |
| 1.8 MPa, Unannealed | 96.1 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 102 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 246 | °C | |
| Middle Temperature | 249 | °C | |
| Front Temperature | 254 | °C | |
| Nozzle Temperature | 260 | °C | |
| Processing (Melt) Temp | 266 | °C | |
| Mold Temperature | 76.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ NEO AG2240 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| NITRIFLEX NP-6000 | NITRIFLEX | NBR | NITRIFLEX |
| 4LOY® 10E27300 | 4Plas | PC+ABS | 4LOY® |
| Colorite 77 Series 6577 | Colorite Polymers | PVC, Unspecified | Colorite 77 Series |
| EMAC+® SP1305 | Westlake Chemical Corporation | EMA | EMAC+® |