SABIC® LDPE 2600H0
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aINdYy_SABIC-LDPE-2600H0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2600H0 is a grade with a low MFR and increased density. The material contains no additives. The films are characterized by very good mechanical properties. Application SABIC® LDPE 2600H0 is, due to its good thin film processability, typically used for technical applications like shrink film for mineral water packaging. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.33 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 220 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 220 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 12.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 28.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 250 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (50.0 µm) | 20 | g | Internal method |
| Re-blocking - Blown Film (50.0 µm) | g | Internal method | |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 35.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 45.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 103 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 57 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 8.0 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at film of 50 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOWLEX™ 5075G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| EPO-TEK® H77 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Keltan® 8550C | LANXESS Buna GmbH | EPDM | Keltan® |
| LG PMMA HI835H | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Ultramid® B27 HM 01 | BASF Corporation | Nylon 6 | Ultramid® |