LNP™ VERTON™ MV008SU compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aIGcAQ_LNPVERTONMV008SUcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* MV008SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. Also known as: LNP* VERTON* Compound MFX-7008 HS UV Product reorder name: MV008SU |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 | g/cm³ | ASTM D792 |
| -- | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.32 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.080 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9560 | MPa | ASTM D638 |
| -- | 10100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 119 | MPa | ASTM D638 |
| Fracture | 127 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.6 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7800 | MPa | ASTM D790 |
| -- | 8260 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 180 | MPa | ASTM D790 |
| -- | 187 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| 23°C 2 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.0 | J | ASTM D3763 |
| -- | 10.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 4 | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 157 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 160 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 - 243 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 249 - 260 | °C | |
| Processing (Melt) Temp | 221 - 249 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3780 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Shandong Nylon A4TR05 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| TECAFINE® PP | Ensinger Inc. | PP Random Copolymer | TECAFINE® |
| THERMOLAST® K TF3BNA (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| POLYFLON™ F-302 | Daikin Fluorochemicals (China) Co., Ltd. | PTFE | POLYFLON™ |