SLOVALEN® PC 59 GB 10
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aHl4ig_SLOVALEN-PC-59-GB-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compouded homopolymer PP, with the content of 10% chemically bound glass beads and modifier of mechanical properties. Increased strength in comparison with unfilled PP. Use in all industry sectors. Delivered in the natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 2.0 | % | |
| Flow | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 20 | kJ/m² | |
| 23°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 100 | °C | ISO 306/B |
| Melting Temperature (DSC) | 150 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Pressure | 60.0 to 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® M-638 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| UBESTA XPA 9055 X2 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| KOPLA PA6 KNG1020F | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| Lumid® SG4389B | LG Chem Ltd. | Nylon 66 | Lumid® |
| SCHULABLEND® (PA/PP) M/MO 5101 | A. Schulman Europe | Nylon+PP | SCHULABLEND® |