| EVAL™ FP101B is an Ethylene Vinyl Alcohol (EVOH) product. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.6 | g/10 min | |
| 210°C/2.16 kg | 3.8 | g/10 min | |
| 230°C/2.16 kg | 6.2 | g/10 min | |
| Ethylene Content | 32.0 | mol% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 83.0 | MPa | |
| Break | 34.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 15 | % | |
| Flexural Modulus | 3800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability 1 | ISO 14663-2 | ||
| 20°C, 0% RH | 4.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 8.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.030 | cm³·mm/m²/atm/24 hr | |
| 20°C, 90% RH | 0.060 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 2 | 1.6 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -- | 2.5 | kJ/m² | |
| -30°C | 1.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 69.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 173 | °C | ISO 306 |
| Melting Temperature | 183 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 161 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Annex C |
| 2 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PBT1460G10 | Guangdong Silver Age Sci & Tech. Co., Ltd | PBT | SILVER® |
| NatureFlex™ 140NP | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| CP PRYME® Nylon 6 N200HSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| Indothene HD HD53MA020 | Reliance Industries Limited | HDPE | Indothene HD |
| Sylvin 9067-90 Grey 9202 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |