Grivory® GVL-5H nat

Category:	Nylon 66+Nylon 6I/X , Polyamide 66 + PA 6I/X
Manufacturer:	EMS-GRIVORY
Trademark:	Grivory®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	aH2Oga_Grivory-GVL-5H-nat.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Grivory® GVL-5H nat is a Polyamide 66 + PA 6I/X (Nylon 66+Nylon 6I/X) material filled with 50% long glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion or injection molding.

Important attributes of Grivory® GVL-5H nat are:

Flame Rated

Heat Stabilizer

Typical applications include:

Automotive

Electrical/Electronic Applications

Appliances

Consumer Goods

Engineering/Industrial Parts

General Information
Filler / Reinforcement	Long Glass Fiber, 50% Filler by Weight
Additive	Heat Stabilizer
Features	Aromatic Heat Stabilized
Uses	Appliance Components Automotive Applications Automotive Exterior Parts Automotive Interior Parts Connectors Consumer Applications Electrical/Electronic Applications Engineering Parts Household Goods Hydraulic Applications Industrial Applications Pneumatic Applications Power/Other Tools Sporting Goods
Appearance	Natural Color
Forms	Granules
Processing Method	Extrusion Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Tensile Modulus vs. Temperature (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.56	--	g/cm³	ISO 1183
Molding Shrinkage				ISO 294-4
Across Flow	0.30	--	%
Flow	0.10	--	%
Water Absorption				ISO 62
Saturation, 23°C	4.0	--	%
Equilibrium, 23°C, 50% RH	1.3	--	%

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	275	260	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	17500	16500	MPa	ISO 527-2
Tensile Stress (Break)	270	235	MPa	ISO 527-2
Tensile Strain (Break)	2.4	2.4	%	ISO 527-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	35	35	kJ/m²
23°C	35	35	kJ/m²
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	90	90	kJ/m²
23°C	110	100	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, Unannealed	255	--	°C	ISO 75-2/A
8.0 MPa, Unannealed	220	--	°C	ISO 75-2/C
Continuous Use Temperature				Internal Method
-- ¹	100 to 120	--	°C
-- ²	220	--	°C
Melting Temperature ³	260	--	°C	ISO 11357-3
CLTE				ISO 11359-2
Flow	2.0E-5	--	cm/cm/°C
Transverse	5.0E-5	--	cm/cm/°C

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	--	1.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+12	1.0E+12	ohms·cm	IEC 60093
Electric Strength	33	33	kV/mm	IEC 60243-1
Comparative Tracking Index	--	600	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flammability Classification (0.800 mm)	HB	--		IEC 60695-11-10, -20

Additional Information	Dry	Conditioned		Test Method
ISO Type	PA66+PA6I/X, MH, 14-180, GF50	--		ISO 1874

Note Message
1 .	Long Term
2 .	Short Term
3 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
SABIC® HDPE M40053S	Saudi Basic Industries Corporation (SABIC)	HDPE Copolymer	SABIC® HDPE
Ultramid® B24 N 03	BASF Corporation	Nylon 6	Ultramid®
BMC 1454	Bulk Molding Compounds, Inc.	Polyester, TS	BMC
Kumho ABS 745	Korea Kumho Petrochemical Co., Ltd.	ABS	Kumho ABS
Hostalen PP H2222 36	LyondellBasell Industries	PP Impact Copolymer	Hostalen PP