LEMALLOY® BX504D
| Category: | PPE+Nylon 6 , Polyphenylene Ether + Nylon 6 |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | LEMALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aGyBG8_LEMALLOY-BX504D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEMALLOY® BX504D is a Polyphenylene Ether + Nylon 6 (PPE+Nylon 6) material filled with filler. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of LEMALLOY® BX504D: Rigid. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.22 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 21.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow : 3.20 mm | 0.60 to 0.80 | -- | % | |
| Flow : 3.20 mm | 0.70 to 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4200 | 2200 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | -- | 42.0 | MPa | |
| Break, 23°C | 62.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | -- | 8.4 | % | |
| Break, 23°C | 6.1 | -- | % | |
| Nominal Tensile Strain at Break (23°C) | -- | 74 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4200 | 2100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 105 | 57.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 12 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | -- | °C | ISO 75-2/A |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 250 to 290 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Nozzle Temperature | 260 to 300 | °C | |
| Mold Temperature | 70.0 to 110 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene Lumicene® BM 359 SG | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| TYNE® ABS CBM 65 | Tyne Plastics LLC. | ABS | TYNE® ABS |
| DURACON® SW-41 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PE | DURACON® |
| Dynaglide® DW 612 | DeWAL Industries | PTFE | Dynaglide® |
| Huafon JF-D-C5902 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |