Kingfa PP-KF08
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aGwMox_Kingfa-PP-KF08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP-T40 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 - 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 - 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | 7.0E-3 - 9.0E-3 | % | Internal method |
| Ash Content 1(750°C) | 38 - 42 | % | ISO 3451 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Long Term Aging (150°C) | > 700.0 | hr | ISO 188 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 32.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 2 | 3500 | MPa | ISO 178 |
| Flexural Stress 3 | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.8 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, unannealed, 4.00mm span) | 130 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 0.0 - 2.0 | hr | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 205 - 230 | °C | |
| Front Temperature | 215 - 240 | °C | |
| Processing (Melt) Temp | 220 - 245 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.350 | MPa |
| Injection instructions |
|---|
| Processing Temp. Limit: 250°C |
| Note Message | |
|---|---|
| 1 . | 30 min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 6604-5 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Silopren® LSR 3486/20 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| BP Flex 9000 VPL BLK | Buckeye Polymers, Inc. | TPV | BP Flex |
| Chemlon® 109-25 GU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Sylvin 4240-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |