Rynite® 415HP NC010
| Category: | PET , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Rynite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aGUxlh_Rynite-415HP-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced Polyethylene Terephthalate with Excellent Impact Resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow 1 | 1.2 | % | |
| Across Flow | 0.80 | % | |
| Flow | 0.30 | % | |
| Flow 2 | 0.50 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 2.5 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.25 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 58 | ||
| R-Scale | 111 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 79.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 3550 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.7 | kJ/m² | |
| 23°C | 13 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Melting Temperature 3 | 250 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Flow : -40 to 23°C | 9.8E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C | |
| Transverse : -40 to 23°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 55 to 160°C | 3.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 19 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Annealed |
| 2 . | Annealed |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PC 740/4 UV WT1310-05LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Boltaron 9815E | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| Elastocon® 8068BL | Elastocon TPE Technologies | TPE | Elastocon® |
| Kumho SSBR SOL-5220M | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| Karina WHITE PVC COMPOUND -E 670D10/116-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |