Lupolen 3426 J
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aG5cVo_Lupolen-3426-J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupolen 3426 J is a low density polyethylene with outstanding high rigidity and excellent optics. It is delivered in pellet form and is additivated with slip and antiblocking agent. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 480 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2 |
| Coefficient of Friction (Blown Film) | < 0.20 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 15 to 60 µm | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, Blown Film | 19.0 | MPa | |
| TD : 50 µm, Blown Film | 16.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 450 | % | |
| TD : Break, 50 µm, Blown Film | 600 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 90 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 109 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 119 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20°, 50.0 µm, Blown Film | > 75 | ||
| 60°, 50.0 µm, Blown Film | > 110 | ||
| Haze (50.0 µm, Blown Film) | < 10 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy - Blown Film (50.0 µm) | 30.0 | J/cm | DIN 53373 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 399 X 115062 F | RTP Company | PC | RTP |
| ROPOTEN® T FV-03-223-2 | LUKOIL Bulgaria Ltd. | LDPE | ROPOTEN® T |
| Sylvin 2990-75 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| UBESTA 3024 LU | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| BCC Resins BC 5105 | BCC Products Inc. | Epoxy | BCC Resins |