Syncure™ System S100BL
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aG2vqb_Syncure-System-S100BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Syncure™ S100BL system is a three part moisture crosslinkable compound. S100BL is a UL bullentinized sunlight resistant, RoHS compliant, low density, black cable insulation compound. Graft resin component of this system has approximate shelf life of 6 months from the date of production. Please consult PolyOne for its use past 6 months. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Gel Content 1 | 68 | % | ASTM D2765 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Tensile strength retention (121°C, 1.91mm) 2 | 95 | % | |
| Elongation retention rate (121°C, 1.91mm) 3 | 90 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation (131°C) 4 | 10 | % | UL 1581 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame test- level | |||
| -- | Pass | CSA FT-2 | |
| -- | Pass | UL 1581 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Catalyst parent mixture | |||
| S-1044B 5 | 5.0 | % | |
| V-0022G RoHS 6 | 16 | % | |
| Transplant-based resin- S-1054A 7 | 79 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 54 | ASTM D2240 | |
| Shaw D, 10 seconds | 49 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 8(Yield) | 19.3 | MPa | ASTM D638 |
| Tensile Elongation 9(Break) | 400 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UL Temperature Rating | 90 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| 注释：以上情况代表了在30密耳壁的14 AWG上测量得出的典型属性。存放和搬运：包装打开之后应在48小时之内使用，避免自硬化和报废。 |
| Note Message | |
|---|---|
| 1 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 2 . | 336 hours, UL standard |
| 3 . | 336 hours, UL standard |
| 4 . | 500g,1 hour |
| 5 . | S-1044B |
| 6 . | V-0022G |
| 7 . | S-1025A or S-1054A |
| 8 . | Type 4, 510mm/min |
| 9 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAN® LFT PP 1335F | SAMBARK | PP, Unspecified | SUPRAN® LFT PP |
| Synthos EPS® 0822F/CZ | Synthos S.A. | PS (EPS) | Synthos EPS® |
| Multiuse Leostomer® LE-3190N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| AURAPENE PPUFBKIMP | Aurora Manufacturing Ltd | TPO | AURAPENE |
| Plenco 06500 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |