LNP™ STAT-KON™ RE007 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aFszoh_LNP-STAT-KON-RE007-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON RE007 is a compound based on PA66 resin containing 35% Carbon Fiber. Added features include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound RC-1007 Product reorder name: RE007 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.33 | g/cm³ | |
| -- | 1.32 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.90 to 1.1 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.59 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.92 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 29900 | MPa | ASTM D638 |
| -- | 30400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 275 | MPa | ASTM D638 |
| Break | 282 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.7 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 24300 | MPa | ASTM D790 |
| -- 5 | 24600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 391 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 387 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 7 | 8.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 8 | 63 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.64 | J | ASTM D3763 |
| -- | 3.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 263 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 262 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 257 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 256 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R130A93 | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyester | Ravathane |
| Sylvin 8215-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Tarnamid® T-27 GF 20 GB 10 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| LEXAN™ FXE141RL resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Jam HD7255* | Jam Petrochemical Company | HDPE | Jam |