Boda BDF25P
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aFgB5d_Boda-BDF25P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDF25P is a low viscosity curative incorporated fluoroelastomer copolymer. This grade is well suited for application where good flowability and excellent mold release property are required. BDF25P can be compounded to meet the major fluoroelastomer specifications. BDF25P can be used for injection molding of O-rings and gaskets or extrusion of complicated geometries. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 25 | MU | |
| Fluorine Content | 66 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.05 | N·m | |
| ML 2(177°C) | 0.170 | N·m | |
| t'90 3(177°C) | 2.2 | min | |
| ts2 4(177°C) | 55.0 | sec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 75 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 13.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 260 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 23 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3400 MG-450 | RTP Company | LCP | RTP |
| UBE Polyethylene F522N | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Celcon® UV270Z | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Eltex® Superstress™ CAP311 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| MAJORIS EC267 - 5753 | AD majoris | PP, Unspecified | MAJORIS |