VESTAMID® E E58-S4
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aErgWA_VESTAMID-E-E58-S4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Typical Applications: specialty grade for transparent sports shoe soles PA 12 elastomers, the most important subgroup of polyamide elastomers, belong to the increasingly important material class of thermoplastic elastomers (TPE). Because of their excellent properties, they are indispensable in many applications. PA 12 elastomers are block copolymers consisting of PA 12 segments and polyether segments. PA 12-rich products have the major properties of PA 12, while the elastomer characteristics become more apparent with increasing polyether content. That is the polymers become more flexible, with higher impact strength at cold temperatures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Viscosity Number | 180 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 58 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 185 | MPa | ISO 527-2 |
| Tensile Stress | 39.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 200 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 5.0 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 55.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 35.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.10 | % | |
| Melt Temperature | 190 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Dryflex® A2 602609 | ELASTO | SEBS | Dryflex® |
| Dynafoam 60% Reduction | Saint Gobain - Norton | TS, Unspecified | Dynafoam |
| Latimass 66-04 D009 | LATI S.p.A. | Nylon 66 | Latimass |
| ISPLEN® PB 141 U5M | REPSOL | PP Impact Copolymer | ISPLEN® |