PULSE™ A35-105
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aEgVa5_PULSE-A35-105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PULSE A35-105 engineering resins give exceptional impact strength even at low temperatures and have a high heat distortion temperature. Applications: PULSE A35-105 is used in a wide range of applications where a balance of low temperature toughness, high heat distortion, and easy processing are required. Some examples are automotive instrument panels, automotive interior/exterior trim, small appliance and electrical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 3.0 | g/10 min | |
| 250°C/5.0 kg | 12 | g/10 min | |
| 260°C/5.0 kg | 17 | g/10 min | |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 to 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 105 | MPa | DIN 53459 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 52.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain (Break) | > 80 | % | ISO 527-2/5 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 126 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ISO 306/A120 |
| -- | 122 | °C | ISO 306/B50 |
| CLTE - Flow (0 to 80°C) | 7.5E-5 to 8.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1(1.60 mm) | HB | Internal Method | |
| Oxygen Index 2 | 20 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R130A85 | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyester | Ravathane |
| ESTAPROP KUR 1520 TG05 | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| ExxonMobil™ LDPE EVA Copolymers LD 363 Series | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| EnviroPC 1512 | West Michigan Compounding | PC | EnviroPC |
| IPC PP 4810H-T | International Polymers Corporation | PP Homopolymer | IPC PP |