OP - PBT INJ
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aEE7D6_OP---PBT-INJ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP-PBT INJ is a polybutene terephthalate (PBT) material,. This product is available in North America and is processed by injection molding. The main characteristics of OP-PBT INJ are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.6 - 2.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 48.3 | MPa | ASTM D638 |
| Fracture | 48.3 | MPa | ASTM D638 |
| Flexural Modulus | 2310 | MPa | ASTM D790 |
| Flexural Strength | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 53 | J/m | ASTM D256 |
| Dart Drop Impact | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Additional Information |
|---|
| Melt Mass- Flow Rate (MFR), ASTM D1238, 210°C / 2.16 kg: 12 to 20 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 - 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 232 - 249 | °C | |
| Middle Temperature | 238 - 254 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 232 - 260 | °C | |
| Mold Temperature | 43.3 - 76.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TP6SKZ (Series: EX/UV) | KRAIBURG TPE | TPE | THERMOLAST® K |
| NEFTEKHIM PE 4118Q (18403) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| APEX® 3211-50NT | Teknor Apex Company | PVC, Flexible | APEX® |
| HAIPLEN EP50 C8 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Hostacom EKC 330N E1 NAT | LyondellBasell Industries | PP Copolymer | Hostacom |