WESTLAKE polyethylene EF403 is a fractional melt low-density formulation suggested for use in clarity shrink applications. This LDPE formula exhibits excellent shrinkability, and has very good optical properties. Application/Uses: Medium duty produce bags Good clarity shrink film Bags for textile items Beverage/Bottle overwrap |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 32 µm, blown film | 179 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, blown film | 221 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 30.3 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 23.4 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 700 | % | ASTM D882 |
| Dart Drop Impact 4(32 µm, Blown Film) | 130 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm, Blown Film) | 75 | ASTM D2457 | |
| Haze (31.8 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.25 mils; blow up ratio 2.5:1, die gap 35 mils.Melt temperatures of 360° F - 390° F are recommended for Westlake Chemical EF403 with blow-up ratios of 1.5:1 or higher. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 199 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A R 130/GF BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| TEKNIFLEX® MED 2001-0200 | Tekni-Films, a div of Tekni-Plex | Film, PP | TEKNIFLEX® MED |
| FERREX® GPP20CK16HB-BK | Ferro Corporation | PP, Unspecified | FERREX® |
| Emulprene® 1028A | INSA | SBR, Emulsion | Emulprene® |
| Hostaform® S 9244 XAP² ™ LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |