VITAMIDE® AR33BK6541
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aCORuK_VITAMIDE-AR33BK6541.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AR33BK6541 is a Polyamide 66 (Nylon 66) product filled with 15% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 160 | MPa | ISO 178 |
| Break | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 255 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 31 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 1804 | Covestro - Polycarbonates | PC | Makrolon® |
| Salflex 623TM4 | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| Witcom PA66 2006/274 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| DynaMix™ 2044-GBD | Polymer Dynamix | Nylon, Unspecified | DynaMix™ |
| Lupol® GP3300 | LG Chem Ltd. | PP, Unspecified | Lupol® |