Eltex® PF6220AA
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aCAdAE_Eltex-PF6220AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Benefits & Features Eltex® PF6220AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
Applications Eltex® PF6220AA has been developed for use in collation shrinkwrap, food packaging and other thin film applications where an excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex® PF6220AA offers easy extrudability. If corona treatment is necessary, the level should be in the range 38-48 mN/m. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm | 160 | MPa | |
| 1% Secant, TD : 25 µm | 195 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 9.00 | MPa | |
| TD : Yield, 25 µm | 10.0 | MPa | |
| MD : Break, 25 µm | 60.0 | MPa | |
| TD : Break, 25 µm | 60.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 620 | % | |
| TD : Break, 25 µm | 700 | % | |
| Dart Drop Impact (25 µm) | 1000 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 220 | g | |
| TD : 25 µm | 450 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature 1 | 104 to 116 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 60 | ASTM D2457 | |
| Haze (25.0 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T20P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Vital-Line SHE6545 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Boltaron 2009 | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| LUVOCOM® 1105/CF/30/EM/L | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| RTP 2200 HF Z | RTP Company | PEEK | RTP |