CALIBRE™ 2060-3
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aC0Uwh_CALIBRE-2060-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 2060-3 Polycarbonate resin is used in medical applications involving steam or ethylene oxide sterilization - though suitability for use in these applications is dependent upon autoclave cycle times and temperatures. CALIBRE 2060-3 provides exceptional clarity, heat resistance, impact strength and has low contamination levels. The CALIBRE 2000 series of resins have been evaluated with respect to ISO 10993-1 (Biological Evaluation of Medical Devices) and are suitable for use in approved medical applications. Main Characteristics
Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 74 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2480 | MPa | ASTM D638 |
| -- | 2480 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 72.4 | MPa | ASTM D638 |
| Break | 72.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2410 | MPa | ASTM D790 |
| -- 6 | 2410 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 96.5 | MPa | ASTM D790 |
| -- 8 | 96.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 960 | J/m | ASTM D256 |
| 23°C | 93 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact (23°C, Total energy) | 93.8 | J | ASTM D3763 |
| Tensile Impact Strength | 630 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 146 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 132 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 143 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 151 | °C | ISO 306/B50, ASTM D1525 9 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance 10(3180 µm) | 89.0 | % | ASTM D1003 |
| Haze 11(3180 µm) | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | Method I (3 point load), 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Method I (3 point load), 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Rate A (50°C/h), Loading 2 (50 N) |
| 10 . | 1/8 inch thickness plaque |
| 11 . | 1/8 inch thickness plaque |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® P copolymer | Röchling Engineering Plastics SE & Co. KG | PP Copolymer | POLYSTONE® |
| SABIC® LDPE 2100TN21 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| EPO-TEK® 301 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Polifil® Nylon 620-33GF | The Plastics Group | Nylon 66 | Polifil® Nylon |
| Stat-Tech™ PP-16CP/000-2HI BLACK | PolyOne Corporation | PP, Unspecified | Stat-Tech™ |