LNP™ THERMOCOMP™ RX06421S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aBSbrh_LNP-THERMOCOMP-RX06421S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RX06421S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Clean Compounding System. Also known as: LNP* THERMOCOMP* Compound RF-1006 EM HS CCS Product reorder name: RX06421S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.39 | g/cm³ | |
| -- | 1.38 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.75 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 181 | MPa | ASTM D638 |
| Break | 181 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.6 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 9620 | MPa | ASTM D790 |
| -- 5 | 9480 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 264 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 92 | J/m | ASTM D256 |
| 23°C 7 | 9.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 970 | J/m | ASTM D4812 |
| 23°C 8 | 57 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.10 | J | ASTM D3763 |
| -- | 2.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 256 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 243 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 239 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 903 | RTP Company | PSU | RTP |
| Multiuse Leostomer® LE-3190N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| Baydur® 728 IBS (35 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Sylvin 8999-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VALOX™ 364 resin | SABIC Innovative Plastics | PBT | VALOX™ |