Generic PC - Carbon Fiber
| Category: | PC , Polycarbonate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aBOlPY_Generic-PC---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.22 - 1.40 | g/cm³ | ASTM D792 |
| 23°C | 1.23 - 1.42 | g/cm³ | ISO 1183 |
| -- | 1.24 - 1.37 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 1.1 - 18 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 3.40 - 10.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.066 - 0.32 | % | ASTM D955 |
| Transverse flow : 23°C | 0.28 - 0.50 | % | ASTM D955 |
| 23°C | 0.065 - 0.51 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.076 - 0.15 | % | ASTM D570 |
| 23°C, 24 hr | 0.14 - 0.20 | % | ISO 62 |
| Saturated, 23°C | 0.070 - 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.095 - 0.21 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 118 - 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 6760 - 19700 | MPa | ASTM D638 |
| 23°C | 6900 - 18200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 87.8 - 148 | MPa | ASTM D638 |
| Yield, 23°C | 56.4 - 144 | MPa | ISO 527-2 |
| Fracture, 23°C | 91.6 - 152 | MPa | ASTM D638 |
| Fracture, 23°C | 88.3 - 152 | MPa | ISO 527-2 |
| 23°C | 95.7 - 165 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 3.1 | % | ASTM D638, ISO 527-2 |
| Fracture, 23°C | 0.90 - 3.8 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5700 - 17000 | MPa | ASTM D790 |
| 23°C | 5870 - 16500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 137 - 243 | MPa | ASTM D790 |
| 23°C | 139 - 227 | MPa | ISO 178 |
| Yield, 23°C | 146 - 177 | MPa | ASTM D790 |
| Fracture, 23°C | 154 - 260 | MPa | ASTM D790 |
| Coefficient of Friction | 0.12 - 0.55 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 22 - 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 48 - 120 | J/m | ASTM D256 |
| 23°C | 5.3 - 9.3 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 340 - 730 | J/m | ASTM D256 |
| 23°C | 20 - 39 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 9.40 - 18.7 | J | ASTM D3763 |
| 23°C | 1.20 - 104 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 139 - 151 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 140 - 152 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 137 - 152 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 134 - 148 | °C | ISO 75-2/A |
| Continuous Use Temperature | 130 | °C | ASTM D794 |
| Vicat Softening Temperature | 151 - 160 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 1.0E-6 - 3.3E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.2E-5 - 1.0E-4 | cm/cm/°C | ASTM E831 |
| Flow | 9.6E-6 - 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-6 - 5.8E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 1.1E-5 - 7.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 4.1E-5 - 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.30 - 0.47 | W/m/K | ISO 8302 |
| RTI Elec | 80.0 - 81.0 | °C | UL 746 |
| RTI Imp | 80.0 - 81.3 | °C | UL 746 |
| RTI | 80.0 - 81.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 2.5 - 6.3E+10 | ohms | ASTM D257 |
| -- | 5.5 - 1.3E+11 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 5.0 - 2.5E+8 | ohms·cm | ASTM D257 |
| 23°C | 0.50 - 1.0E+4 | ohms·cm | IEC 60093 |
| Insulation Resistance (23°C) | 1.0E+2 - 2.5E+7 | ohms | IEC 60167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 122 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.022 | % | |
| Rear Temperature | 288 - 316 | °C | |
| Middle Temperature | 300 - 317 | °C | |
| Front Temperature | 300 - 328 | °C | |
| Nozzle Temperature | 300 - 301 | °C | |
| Processing (Melt) Temp | 295 - 317 | °C | |
| Mold Temperature | 92.5 - 103 | °C | |
| Injection Pressure | 86.0 - 121 | MPa | |
| Back Pressure | 0.232 - 0.305 | MPa | |
| Screw Speed | 45 - 46 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1000 HI UV | RTP Company | PBT | RTP |
| Nypol® PA A3 G50 HS RH PRTA012 NR439 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Colorite 77 Series 7577 | Colorite Polymers | PVC, Unspecified | Colorite 77 Series |
| Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-ACE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EPALINE 392A55 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPALINE |