INSTRUC PPGF10
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aB3Yi8_INSTRUC-PPGF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% GLASS FIBER REINFORCED POLYPROPYLENE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 37.9 | MPa | ASTM D638 |
| Flexural Modulus | 2140 | MPa | ASTM D790 |
| Flexural Strength | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact | 430 to 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 193 to 227 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 3585 | Huntsman Corporation | PAO | REXtac® APAO |
| Starflam MX06101 | Eurostar Engineering Plastics | PP, Unspecified | Starflam |
| CastForm™ PS | 3D Systems | PS (Specialty) | CastForm™ |
| Elastron® V P.V101.A90.B | Elastron USA, Inc. | TPV | Elastron® V |
| Sumiliteresin® ECP-294 | SBHPP | Epoxy | Sumiliteresin® |