Preliminary Data Sheet Hostaform® LX90 specialty metallic appearance grades are an integrally colored nominal 9 melt flow rate based acetal copolymer material formulated to provide an exceptional molded in metallic appearance. This product is available in many metallic molded-in-colors. Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.75 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 56.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 88.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 175 | °C | |
| Middle Temperature | 170 - 180 | °C | |
| Front Temperature | 175 - 185 | °C | |
| Nozzle Temperature | 185 - 195 | °C | |
| Processing (Melt) Temp | 180 - 195 | °C | |
| Mold Temperature | 80.0 - 105 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 180 to 200°CZone 4 Temperature: 180 to 190°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toughblend® PC-1200 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC | Toughblend® |
| Karina WHITE PVC COMPOUND 801-10/ 95-A-ERYB (**) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina MBPP GREEN 4000/141-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polimid B 40 | Poliblend S.p.a. | Nylon 6 | Polimid B |
| Sylvin 6229-70LG Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |