| PLENCO 03554 is an organic reinforced phenolic molding compound modified with PTFE to offer improved coefficient of friction values. 03554 is available in black. It is UL listed. 03554 is a re-number of 06554 formulation. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Apparent Density | 0.57 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.43 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.43 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638 |
| Tensile Strength | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 7670 | MPa | ASTM D790 |
| Flexural Strength | 81.6 | MPa | ASTM D790 |
| Compressive Strength | 153 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 22.5 | J/m | ASTM D256 |
| Notched Izod Impact | 23 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 157 | °C | ASTM D648 |
| Continuous Use Temperature | 190 | °C | ASTM D794 |
| CLTE - Flow | 9.9E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity (100°C) | 0.37 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.8E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 16 | kV/mm | ASTM D149 |
| -- 2 | 9.0 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.042 | ASTM D150 | |
| Arc Resistance | 73.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177 was tested according to the ASTM E1461 standard.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.15%Heat Resistance, ASTM D794: 190°CDrop Ball Impact, PLENCO Method: 155 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Mold Close Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 90690A-89 BLACK | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| APEX® 2590-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Exelene® PP C0800 | Montachem International, Inc. | PP Impact Copolymer | Exelene® PP |
| EPO-TEK® CF6-2 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| MAXATEL® AC109TF20-BK | Pier One Polymers, Inc. | Acetal (POM) Copolymer | MAXATEL® |