E-RIALFILL C HB 20 T
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a8wLmf_E-RIALFILL-C-HB-20-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene compound copolymer, 20% filled with selected talc. High flowability specific for injection molding, good dimensional stability and excellent compromise between impact strength and stiffness up to low temperatures; available inthe version of natural color and colored as per sample; the black is listed HB according to the norms of UL-94, file E178416. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 | % | |
| Flow | 1.2 | % | |
| Ash Content | 20 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 25.0 | MPa | |
| Break, 23°C | 18.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 8.0 | % | |
| Break, 23°C | 100 | % | |
| Flexural Modulus 1(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.0 | kJ/m² | |
| -20°C | 3.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 76.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9656-45 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ PX0844 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Fiberfil® PP-60/VO/NH | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Pier One POM AC109-BK09 | Pier One Polymers, Inc. | Acetal (POM) Copolymer | Pier One POM |
| ESTOPLAST EP 2030BR27 | Ester Industries Ltd. | PBT | ESTOPLAST EP |