Elastollan® S98AN
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a8D4RA_Elastollan-S98AN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® S98AN is specifically formulated for injection molding applications with short cycling time. It exhibits good hydrolytic stability, excellent abrasion resistance, toughness, good heat, oil, fuel, and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® S98AN is supplied uncolored in diced form. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 131 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 138 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 50.0 | mg | ASTM D1044 |
| Abrasion - DIN | 35 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 133 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 21.4 | MPa | |
| 300% Strain | 40.7 | MPa | |
| Tensile Strength | 46.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 420 | % | ASTM D412 |
| Tear Strength 1 | 210 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 30 | % | |
| 70°C, 22 hr | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -14.0 | °C | Internal Method |
| Vicat Softening Temperature | 157 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P885RSUA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| T-Blend® 0092N-NE | TSRC Corporation | SEBS | T-Blend® |
| Epoxies, Ect. 20-3006 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| LUVOCOM® 100-8758 | Lehmann & Voss & Co. | PUR, Unspecified | LUVOCOM® |
| PLUSTEK RA307G4 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |