BCC Resins BC 8400
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a84Af8_BCC-Resins-BC-8400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BC 8400 is an unfilled, low viscosity, quick setting two component urethane system. An easy to use 1 to 1 mix ratio (Part A/Part B), BC 8400 offers the user a 3 minute working time with parts demoldable in as little as 30 minutes. When properly cured, BC 8400 will exhibit high impact strength and yield thermoplastic-like parts. Some outstanding features include the following: mercury free, moderate heat resistance, 1 to 1 mix ratio, turn white upon cure, longer mold life, high impact strength, no objectionable odor, excellent finishing properties, thermoplastic appearance, more parts per day. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.25 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 36.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 13 | % | ASTM D638 |
| Flexural Modulus | 1730 | MPa | ASTM D790 |
| Flexural Strength (Break) | 60.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 72 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 62.8 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Resin | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Pot Life | 3.0 | min | |
| Thermoset Mix Viscosity (24°C) | 190 | cP | ASTM D2393 |
| Demold Time (25°C) | 30 to 60 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VisiJet® CR-WT | 3D Systems | Unspecified | VisiJet® |
| NEFTEKHIM PE 4020R (20405) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| NatureFlex™ NP 140 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Escorene™ Ultra UL 8705 Series | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| LNP™ LUBRICOMP™ JCL36E compound | SABIC Innovative Plastics | PESU | LNP™ LUBRICOMP™ |