LNP™ LUBRICOMP™ RL0049S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a7NwNt_LNP-LUBRICOMP-RL0049S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RL-4040 FR HS Product reorder name: RL0049S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.5 | % | |
| Across Flow : 24 hr | 1.7 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.39 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.55 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3180 | MPa | ASTM D638 |
| -- | 3170 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 47.3 | MPa | ASTM D638 |
| Break | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.2 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3100 | MPa | ASTM D790 |
| -- | 2970 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 77.6 | MPa | ASTM D790 |
| -- | 78.7 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 21 | J/m | ASTM D256 |
| 23°C 2 | 2.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D4812 |
| 23°C 3 | 11 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 0.570 | J | ASTM D3763 |
| -- | 0.740 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 90.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 105 HB | RTP Company | PP, Unspecified | RTP |
| Sinpolene GPP5630/8 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Expandable PS RF23W | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| DynaPath™ C3850CF | Polymer Dynamix | PPS | DynaPath™ |
| Hostacom HBG H01 NAT | LyondellBasell Industries | PP Homopolymer | Hostacom |