NYLEM® 66 GFR 35 FR V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EMAS Plastik San.Tic.AS. |
| Trademark: | NYLEM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a71ZQG_NYLEM-66-GFR-35-FR-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, %35 glass fiber reinforced, V0 flammability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 to 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.15 to 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 to 11000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 180 to 230 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | > 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | °C | ISO 306/B |
| Melting Temperature (DSC) | 265 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | VDE 0471/2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5153-89 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polystyrene Crystal 1810 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Unichem 7811 Radiopaque-65 | Colorite Polymers | PVC, Unspecified | Unichem |
| Edgetek™ ET3300-5007 Natural FD | PolyOne Corporation | PBT | Edgetek™ |
| Epoxies, Ect. 50-3152 FR | Epoxies, Etc. | Epoxy | Epoxies, Ect. |