Starex TX-0550
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a70Yqx_StarexTX0550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex TX-0550 is a methyl methacrylate/ABS (MABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Starex TX-0550 applications include electrical appliances and consumer goods. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| natural color | 1.09 | g/cm³ | ASTM D792 |
| natural color | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 25 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 26 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.40 - 0.80 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.40 - 0.80 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.60 | % | ISO 2577 |
| Traffic : 3.20mm | 0.40 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 110 | ASTM D785 | |
| R scale | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 41.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 43.0 | MPa | ASTM D638 |
| Fracture | 47.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 25 | % | ASTM D638 |
| Fracture | 25 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 64.0 | MPa | ASTM D790 |
| -- 8 | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 130 | J/m | ASTM D256 |
| 23°C 10 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 76.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 85.0 86.0 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-2000GP | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| ADMER™ NF408E | Mitsui Chemicals Europe GmbH | PE, Unspecified | ADMER™ |
| Geon™ Vinyl Flexible G92D | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hyundai EP XLPE XP460/Natural | HYUNDAI EP Co., Ltd. | XLPE | Hyundai EP XLPE |
| Mafill® CR XT 4644 | Ravago Group | PP, Unspecified | Mafill® |