HIVAL® 1609 NAT
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Nexeo Solutions, LLC. |
| Trademark: | HIVAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a6URA4_HIVAL-1609-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HIVAL®1609 NAT is a polyoxymethylene (POM) copolymer material,. This product is available in North America and is processed by injection molding. HIVAL®The main features of 1609 NAT are: ROHS certification. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2650 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 35 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 154 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 98.9 | °C | ASTM D648 |
| Peak Melting Temperature | 167 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 191 - 210 | °C | |
| Middle Temperature | 210 - 216 | °C | |
| Front Temperature | 218 - 227 | °C | |
| Nozzle Temperature | 218 - 227 | °C | |
| Processing (Melt) Temp | 191 - 229 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Back Pressure | 1.03 - 3.45 | MPa |
| Injection instructions |
|---|
| Injection Speed: Slow - FastAvoid excessive melt temperatures and long residence times as this could lead to thermal degradation. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene CPP2040 | Teknor Apex Asia Pacific PTE. LTD. | PP Copolymer | Sinpolene |
| WPP PP WPP331 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| LUVOCOM® 1800-7432 | Lehmann & Voss & Co. | PET | LUVOCOM® |
| PAmpellonne® 615 | Politem Plastik Ltd. | Nylon 6 | PAmpellonne® |
| Sylvin 6250-82 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |