Generic PP Copolymer - Calcium Carbonate
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a6280q_Generic-PP-Copolymer---Calcium-Carbonate.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer - Calcium Carbonate This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.941 - 1.26 | g/cm³ | ASTM D792 |
| 23°C | 0.968 - 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 9.4 - 20 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 5.9 - 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.87 - 1.8 | % | ASTM D955 |
| Transverse flow : 23°C | 1.4 - 1.7 | % | ASTM D955 |
| 23°C | 1.0 - 1.3 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 - 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 44 - 88 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 66 - 71 | ASTM D2240 | |
| 23°C | 65 - 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 239 - 2410 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 13.0 - 27.8 | MPa | ASTM D638 |
| Yield, 23°C | 14.8 - 30.1 | MPa | ISO 527-2 |
| Fracture, 23°C | 11.0 - 18.3 | MPa | ASTM D638 |
| 23°C | 16.3 - 23.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 12 | % | ASTM D638 |
| Yield, 23°C | 2.8 - 9.7 | % | ISO 527-2 |
| Fracture, 23°C | 5.0 - 210 | % | ASTM D638 |
| Fracture, 23°C | 2.7 - 72 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 890 - 1940 | MPa | ASTM D790 |
| 23°C | 1170 - 2340 | MPa | ISO 178 |
| Flexural Strength (23°C) | 15.5 - 41.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 - 160 | J/m | ASTM D256 |
| 23°C | 3.4 - 8.2 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 1200 - 1300 | J/m | ASTM D256 |
| 23°C | 9.0 - 29 | kJ/m² | ISO 180 |
| Dart Drop Impact (23°C) | 0.565 - 18.2 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 13.4 - 33.9 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 50.0 - 112 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 75.0 - 131 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 43.6 - 61.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 48.0 - 65.1 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 65.0 - 154 | °C | ISO 306 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 - 93.3 | °C | |
| Drying Time | 1.0 - 3.0 | hr | |
| Rear Temperature | 200 - 246 | °C | |
| Middle Temperature | 200 - 246 | °C | |
| Front Temperature | 199 - 246 | °C | |
| Nozzle Temperature | 188 - 238 | °C | |
| Processing (Melt) Temp | 180 - 216 | °C | |
| Mold Temperature | 32.2 - 49.4 | °C | |
| Injection Pressure | 5.86 - 88.2 | MPa | |
| Back Pressure | 0.328 - 1.10 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Copolymer - Calcium CarbonateThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 150 LF | RTP Company | PP, Unspecified | RTP |
| XYRON™ T0702 | Asahi Kasei Chemicals Corporation | PPE+PP | XYRON™ |
| COTENE™ M1208 ES | ICO Polymers EMEA, A Division of A. Schulman | Polyolefin, Unspecified | COTENE™ |
| Ferro PP LPP10BK38BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Iupital® F20-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |